Hi, I can confirm that ! The paths are not really closed. I think this is a similar function such as "clip" in skeinforge or the "coast" function in simplify, to avoid blobs at the end of a path. If you print only one solid object there is no big impact... But if you print more objects, especially with single walls, the objects are not watertight. Second problem is, the travel moves between thvon NitroXpress - Slic3r
Hi, das was Du suchst, nennt sich "clip". Funktioniert recht gut bei Deiner beschriebenen Problematik. Macht aber zum Teil andere Probleme, wenn das Ende z.B. in einem Bogen liegt. Allerdings kommen da auch noch andere Faktoren ins Spiel. Du kannst auch mal die Reihenfolge für Perimeter usw. ändern. Von Aussen nach Innen sieht normalerweise besser aus, macht aber wiederum bei Überhängen Problemvon NitroXpress - Software
Hi Dave, thanks for the SCAD script. But in between i have made attempts with more than 300000 facetes on this simple cylinder. (.stl file with 15MB's !) Now i am 100% certain, that there is no problem with the model resolution. CURA for example, generates 350 segments with this model. That's what i expect ! Unfortunately I expect no help from slic3r developer side... So inevitably, i will covon NitroXpress - Slic3r
Sorry Roger, I misunderstood your question. But what is the problem you have with the support function ? I don't use support very often and i know, the automatic support is not perfect. But with threshold value it should work... If you want, i can can give you a simple calibration object, which is very helpful for adjusting the threshold value. Frankvon NitroXpress - Slic3r
Hi Roger, the sources are here. Download the .zip archive. A description for windows build is here. Frankvon NitroXpress - Slic3r
Hi Dave, I did some more experiments... Let's say 128 is the highest number of segments for a "50mm cylinder", that slic3r can produce. Now a simple calculation : 50*3,14= 157mm circumference 157/128=1,23mm radians So let's just say we have a segment length of ~1,23mm (mathematically not correct because we have 128 chords of a circle) Than i did a slice of a "10mm cylinder" with 1° angle revon NitroXpress - Slic3r
Hi Dave, here you can see a typical print object :-) The "beer-glass" is 380mm high. 0,18mm single wall. Printed with 240mm/sec and up to 320mm/sec. And it is waterproof ! If you look just enough you can see the water drops inside and through the wall. But I want more... Frankvon NitroXpress - Slic3r
Damned... Same problem as in my file. Exactly 128 segments I have tried it with many different CAD programs and same effect every time. That must be a problem with all slicers and the minimum segment length. Can you export it with 2° resolution ? I want to know if there are 188 segments like with my model. I can see the facetes in my prints because i often print thinwall objects with 0,2mm.von NitroXpress - Slic3r
Hi Dave, I've made a few experiments with the CAD Output. It seems that 2° is the optimal angle at 50mm diameter to force slic3r output at highest resolution. If I go 0.1° higher or lower slic3r reduces the number of segments. I can force my CAD Software to output segments with edge length not more than x.xx, if that's the problem. But what is the optimal value for all diameters ? I have chavon NitroXpress - Slic3r
Hi Dave, yes I am pretty certain. You can see the different resolutions already on the file sizes. I made a single wall with no retraction and counted the segments in the RepetierHost Preview one by one. Have you sliced the second file too ? I have opened a Feature Request at GitHub but Alessandro closed it very quick... If I did something wrong, shame on me and I am very sorry. But I don'tvon NitroXpress - Slic3r
I forced the output of my CAD Software to decrease the number of vertices. Output resolution is now 2° (180 segments) Now Slic3r generates 188 segments. How is that ? I am very confused... Frankvon NitroXpress - Slic3r
Yes, you are right. This is mainly a effect of mechanic and trajectory generation. At a lower speed the mechanic and the trajectory generation can move the head more accurate at the original path. Therefore i asked about the minimum segment length in my other thread... Frankvon NitroXpress - Slic3r
Yes, decreasing speed is often a solution for many printing problems... But it's not the "cure"... It's important to have the perfect interaction between printhead moves and extruder flow. For example look at the attached picture. I made a thinwalled tube 25mm diameter, 100mm high. Wall thickness is 0,2mm. Every 10mm of Z-high i increased the velocity about 10mm/sec. Starting with the "standavon NitroXpress - Slic3r
Hi Falk, indeed it is a interaction of many slicing and firmware settings. For this model CURA is the better choice, because the higher slicing resolution and more precise extrusion calculation, also depending on model resolution. A worse model/slicing resolution causes acceleration/deceleration peaks. For a smooth surface it is important to have a steady trajectory generation. You can countevon NitroXpress - Slic3r
Hi, can you attach the original .stl model ? Frankvon NitroXpress - Slic3r
Hi Dave, here is the 50mm cylinder in high resolution. If slic3r follows the original resolution it should generate 360 segments. I know, this restriction is because a standard RepRap controller can not handle such a data flood. But i have a very fast CNC controller with ethernet connection. So he can handle 0,2mm segments at 400mm/sec and more... Frankvon NitroXpress - Slic3r
Hi all, I wonder, if it's possible to adjust the min. segment length. It seems that Slic3r cannot create more than 128 segments for a circle. I have a 50mm diameter cylinder created with a angle resolution of 1° (360 segments) But Slic3r output is only 128 segments. Cura for example creates up to 250 segments... Frankvon NitroXpress - Slic3r
Hi, sliced without a problem (V1.1.7) at 1 and 2 Perimeters. There are 119 intersecting triangles but still manifold... Frankvon NitroXpress - Slic3r
Hi, in the Fill Tab you have to choose 1 Extra Shell on Sparse Layer. Frankvon NitroXpress - Skeinforge
Hi, the retract parameters are in the dimension tab. I recommend to use the absolut dimension for the e-axis value. But, i think you forgot to set the e-axis (extruder) to zero. You can simply do this by adding the following command line to the start code: G92 E0 Have fun... Frankvon NitroXpress - Skeinforge
Hi, in the export plugin, you have to choose "small G-Code" All redundant commands will be removed. Also you can remove comments. Frankvon NitroXpress - Skeinforge
Hi, Du must beim .stl Export noch die Einheiten einstellen. Wenn Du den .stl Export machst, auf "Optionen" unten im Fenster klicken. Im nachfolgenden Fenster oben links unter "Binär" werden die Einheiten in einem Pulldown ausgewählt. Weiter unten im Fenster kannst Du auch noch die Auflösung der .stl Datei beeinflussen. Gruss Frankvon NitroXpress - Software
Hi, MOI (Moment of Inspiration) ist eine sehr gute Software für die Modellerstellung. Sehr leicht zu erlernen und der .stl Export ist prima. Ausserdem gibt es schon viele kostenlose User Plugins dafür. Die Entwicklung geht auch ständig weiter. Eine 30 Tage Demo gibts auch. Gabs bei Filou vor ein paar Tagen noch zum Einführungspreis von 199€ + Märchensteuer. Ich nutze die Software jetzt schon evon NitroXpress - Software
Hi, ich habe seit ein paar Wochen MOI 3D (Moment of Inspiration) im Einsatz. Gibts laut Newsletter noch bis zum 15.01.2014 zum Einführungspreis von 199 + Märchensteuer. Sehr leicht zu erlernende Software. Kann ich nur empfehlen ! Wird auch ständig weiterentwickelt und es gibt User Plugins dafür. Inventor ist zu "overdosed" für 3D Druck. Einziges Manko ist, dass sich vorhandene .stl Dateienvon NitroXpress - Software
Hi Holger, leider entspricht der extrudierte Durchmesser nicht unbedingt genau dem Durchmesser der Düse. Deswegen ist es wichtig den extrudierten Durchmesser zu kennen um Skeinforge dann entsprechend anzupassen. Wenn Du z.B. eine 0,4mm Düse hast (im Idealfall 0,4mm frei extrudiertes Filament) , solltest Du nicht unter 0,3mm Layerhöhe gehen. Sonst "ziehst" Du das Material zu stark, was dann wiedvon NitroXpress - Allgemeines
Hi Holger, von einem Mendel90 bin ich wesentlich besseres gewohnt, was die Qualität anbelangt ! Da hast noch einiges an Einstellarbeiten vor Dir... Wie Gerhard schon geschrieben hat, gibt es ein paar Dinge die perfekt aufeinander abgestimmt sein sollten. Freut mich, dass Du Dich an Skeinforge rangetraut hast. Ist meines Erachtens immer noch mit Abstand der beste Slicer, bis auf ein paar kleinevon NitroXpress - Allgemeines
Hi Luke, ich würde die Finger von dem Ding lassen... Wenn ich sehe, dass die Linearlager mit Kabelbinder einfach so rangetüdelt sind, wird mir schon schlecht. Dann noch ein Reibradantrieb, Naja... Auch sehe ich an dem Ding kein Potential, noch was zu pimpen. Wenn Du mich fragst ist das rausgeschmissenes Geld. Spar lieber noch und bau Dir einen Mendel90. Gruss Frankvon NitroXpress - Allgemeines
Hi Stefan, ich habe auch hin und wieder das Problem, dass das Filament bricht. Auch bei Filament verschiedenster Hersteller. Da mein Drucker in einem nur zeitweise beheizten Raum steht, sinkt die Temperatur gerne mal bis auf 17° ab. Erst ab einer Raumtemperatur von 22-23 Grad läuft es wieder problemlos. Zur Zeit lege ich die Filamentrolle vorher eine Weile auf die Nachstpeicherheizung damit sivon NitroXpress - Extruder, Hotends & verschiedene Materialien
Hallo Gerhard, eventuell musst Du die Einstellungen für den Thermistor in der Steuerung anpassen. Es wäre denkbar, dass die Temperatur nicht stimmt... Laut E3D Doku wird ein EPCOS B57560G104 verwendet. Falls Du einen Bausatz von E3D gekauft hast, solltest Du auch den korrekten Zusammenbau nochmal überprüfen. Zwischen Düse und Heizblock sollte ein kleiner Spalt sein. Gruss Frankvon NitroXpress - Extruder, Hotends & verschiedene Materialien